| Working Life | >5000 h | Place of Origin | Hunan,China |
| Packaging Details | Inner vacuum packaging, outside carton. | Product Name | Microwave Magnetron Ceramic |
| Working Voltage | 3v~480v | Material | 95% aluminum oxide |
| Power Range | ≤7W /cm2 | Model Number | AD-M010 |
| Supply Ability | Full Supply | Density | 3.7g/cm3-5.9g/cm3 |
| High Light | Microwave Magnetron Ceramic / Ceramic Parts / Metallized Ceramic | Certification | / |
| Brand Name | Antaeus | Payment Terms | T/T or Negotiation |
| Price | Negotiation | Delivery Time | 15-45 days |
| Minimum Order Quantity | Negotiation | Working Temperature | -40℃-125℃ |
| Application | Microwave Magnetron Ceramic for Home Electrical Appliances | Thermal Shock Test | 1.(Temperature)：-55℃/125℃ 2,(Time)2.2min 3 (Switching time ) Max 10s 4 (Frequency)：15 times |
Microwave Magnetron Ceramic Parts / Ceramic Ring for Home Electrical Appliances
1. Description:
Alumina Ceramic have a high melting point, high hardness,although mechanical strength is reduced at temperatures above 1000 C. Due to the relatively large coefficient of thermal expansion, thermal shock resistance is reduced. So it is widely used for many mechanical parts which request very high temperature.
Aluminum Oxide, or alumina, is the most common technical ceramic material used today. The versatility of alumina stems from its broadly impressive material properties, ease of manufacture, wide availability, and budget-friendly cost. STC produces a range of alumina purity from 74% alumina to 99.96% alumina - these bodies are the industry work-horse materials for applications that require electrical isolation, wear resistance, high temperature resistance, and good mechanical strength.Alumina sees application from aerospace to medical, from bearings to analytical instrumentation, from electrical standoffs to semiconductor processing. In addition, these materials lend themselves well to be hermetically sealed to metals through metallizing and brazing methods.
2. Feature Advantages:
1) High elasticity modulus
2) High compressive strength.
3) Anti corrosion
4) Abrasion resistance
5) Impact resistance
6) High precision
7) High stability
8) Good advanced ceramic materials
9) High welding sealing performance
10) High hardness and high density
11) Low thermal conductivity
12) Chemical inertness
13) Good wear resistance
14) High Fracture toughness
15) Good insulation performance
16) High temperature resistance
3. Material Features / Properties:
| Color | White or Ivory | White or Ivory | White or Ivory | |
| Density | g/cm 3 | 3.82 | 3.9 | 3.92 |
| Hardness | HRA | 83 | 85 | 85 |
| Flexural Strength | Mpa (psi*10 3 ) | 375 | 386 | 381 |
4. Technical Parameters:
| Technical Parameters of Ceramics | ||||||||
| Items | Test Conditions | Unit or Symbol | 99% AL2O3 | 95% AL2O3 | 90% AL2O3 | Zirconia | Steatite | Silicon Carbide |
| Volume Density | -- | g/cm3 | ≥3.70 | ≥3.62 | ≥3.40 | ≥5.90 | ≥2.60 | ≥3.08 |
| Tightness | -- | Pa·m³/s | ≤1.0×10-11 | ≤1.0×10-11 | ≤1.0×10-11 | - | - | - |
| Liquid Permeability | -- | -- | Pass | Pass | Pass | Pass | - | |
| Flexural Strength | - | MPa | ≥300 | ≥280 | ≥230 | ≥1100 | ≥120 | ≥400 |
| Elastic Modulus | - | GPa | - | ≥280 | ≥250 | ≥220 | - | 400 |
| Poisson Ratio | - | - | - | 0.20～0.25 | 0.20～0.25 | - | - | - |
| Thermal Shock Resistance | 800℃( Room Temperature) Cycle: 10 times | Pass | Pass | Pass | - | - | - | |
| Coefficient of Linear Expansion | 20℃～100℃ | ×10-6 K-1 | - | - | - | ≤8 | - | |
| 20℃～500℃ | ×10-6 K-1 | 6.5～7.5 | 6.5～7.5 | 6.5～7.5 | 6.5～11.2 | - | - | |
| 20℃～800℃ | ×10-6 K-1 | 6.5～8.0 | 6.5～8.0 | 6.3～7.3 | - | 4 | ||
| 20℃～1200℃ | ×10-6 K-1 | - | 7.0～8.5 | - | - | - | - | |
| Coefficient of Thermal Conductivity | 20℃ | W/(m·k) | - | - | - | - | - | 90～110 |
| 1000℃ | ||||||||
| Dielectric Constant | 1MHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | ≤7.5 | - |
| 1MHz 50℃ | - | - | 9.0～10 | - | - | - | - | |
| 10GHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | - | - | |
| Volume Resistivity | 100℃ | Ω·cm | ≥1.0×1013 | ≥1.0×1013 | ≥1.0×1013 | - | ≥1.0×1012 | - |
| 300℃ | ≥1.0×1013 | ≥1.0×1010 | ≥1.0×1013 | - | - | - | ||
| 500℃ | ≥1.0×109 | ≥1.0×108 | -- | - | - | - | ||
| Disruptive Strength | D.C | kV/mm | ≥17 | ≥15 | ≥15 | - | ≥20 | - |
| Chemical Durability | 1:9HCl | mg/c㎡ | ≤0.7 | ≤7.0 | - | - | - | - |
| 10%NaOH | mg/c㎡ | ≤0.1 | ≤0.2 | - | -- | - | - | |
| Grain Size | - | μm | - | 3~12 | - | - | - | - |
5. Process Flows:
Formulating --- Granulating --- Forming --- Sintering --- Grinding --- Printing --- Nickel Plating --- Inspecting --- Packing
6. Application Fields:
Microwave Magnetron Ceramic for Home Electrical Appliances , Aerospace and Other Industry!
7. Production Facilities: Prilling Tower , Forming Machine , High Temperature Sintering Kiln
8. Detection Devices:
Electric Performance Tester , Film Thickness Analyzer , Granulometer , Helium Mass Spectrometer Leak Detector , Universal Pull Force Meter
9. Notes:Above information only for reference and please contact with us for more details freely when you have any inquiry!