| Price | USD 30～50/KG |
| MOQ | 30kg |
| Delivery Time | 10～15 Working days |
| Brand | CUBERYLLIUM |
| Place of Origin | China |
| Certification | ISO ROHS |
| Model Number | CuCo2Be |
| Packaging Details | Pack in coil+waterproofing winding film+Drier+Wooden Case |
| Payment Terms | L/C, T/T |
| Supply Ability | 50T/Month |
| Tensile Strength | 680~900 Mpa | Place of Origin | China |
| Electrical conductivity | 45~60% IACS | Packaging Details | Pack in coil+waterproofing winding film+Drier+Wooden Case |
| Specification | 8*500mm | Model Number | CuCo2Be |
| Hardness | B92~100 Rockwell B Scale | Supply Ability | 50T/Month |
| Typical Application | Electrical Industry | Certification | ISO ROHS |
| Name | Beryllium Copper C17500 Round Bar | Surface | Bright |
| Shape for available | Rod&Bar | Elongation Percent | 10~30 Min |
| Brand Name | CUBERYLLIUM | Payment Terms | L/C, T/T |
| Brand | CUBERYLLIUM® | Heat Treatment | 3 hr 480℃ |
| Price | USD 30～50/KG | Delivery Time | 10～15 Working days |
| ASTM | ASTM B441 | State | AT(TF00) |
| Minimum Order Quantity | 30kg |
Corrosion-Resistant Beryllium Copper C17500 Round Bar Size 8*500mm Used For Resistance Welding Equipment
Product Description:
Name: Beryllium Copper C17500 Round Bar
Grade: C17500
End Product Form: Rod/ Bar
Standard: ASTM B441
Processing: Seamless / Welding
Feature: Corrosion-resistant
Package: Pack in coil+waterproofing winding film+Drier+Wooden Case
Specification: 8*500mm
Introduction of Beryllium Copper C17500:
| Element | Alloy C17500 has a Chemical Formula of Becu. |
|---|---|
| Different Name of Beryllium Copper | Beryllium Bronze, Copper Beryllium (CuBe), Spring Copper |
| Feature | C17500 has moderate strength and its conductivity is around 50%. |
| Application | C17500 alloy is used in a wide variety of industrial processes in resistance welding equipment, switch parts, spring connectors, fasteners, fuse clips, die–casting plunger tips, springs, resistance and spot welding tips, connectors, seam welding dies, relay parts, tooling for plastic moulds, washers, etc. It is available in sheets, round tubes, rectangular bars, flat bars, round wires, coils, square bars, plates, round bars, hexagon bars and various custom made shapes. |
Chemical Composition of Beryllium Copper C17500 Alloys:
| CUBERYLLIUM® Brand | UNS-Number | Beryllium | Cobalt | Nickel | Cobalt+Nickel | Lead | Copper |
| Cuberyllium-C750 | C17500 | 0.40-0.70 | 2.4～2.7 | - | - | - | Balance |
Related material specifications of Beryllium Copper C17500 Alloys:
Rods/Bars/Tubes: ASTM B441, SAE J461, 463; RWMA Class 3
Strips: ASTM B534
Sheets: ASTM B534
Wires: ASTM B441
Plates: ASTM B534, SAE J461, RWMA Class 3
European Standards: CuCo2Be, CuCoBe, UNS. C17500, Alloy 10, DIN 2.1285, CW104C to EN
Note:
ASTM: American Society for Testing and Materials
SAE: Society of Automotive Engineers
AMS: Aerospace Materials Specification(Published by SEA)
RWMA: Resistance Welder Manufacturers' Association
Note: Unless otherwise specified, material will be produced by ASTM.
Typical
Physical
Properties
of
Beryllium
Copper
C17500
Alloys:
| Density | 8.83 | g/cm3 |
| Density before age hardening | 8.75 | g/cm3 |
| Melting Range | 1000~1070 | ℃ |
| Elastic Modulus | 14.1 | (kg/mm2 (103) |
| Thermal Expansion Coefficient | 18 x 10 -6 | 20 °C to 200 °C m/m/°C |
| Thermal Conductivity | 0.48 | cal/(cm-s-°C) |
Mechanical and Electrical Properties of Copper Beryllium Rod&Bar and Tube of CUBERYLLIUM®-750:
| Temper(*) | Diameter | Heat Treatment |
Tensile Strength Mpa |
Elongation Percent (Min) |
Electrical Conductivity Percent IACS |
Hardness Rockwell B Scale |
|---|---|---|---|---|---|---|
| A(TB00) | ALL SIZE | / | 240~380 | 20~40 | 20~35 | B20~50 |
|
H(TD04) |
ALL SIZE | / | 440~550 | 10~20 | 20~35 | B20~30 |
| AT(TF00) | ALL SIZE | 3 hr 480℃ | 680~900 | 10~30 | 45~60 | B92~100 |
| HT(TH04 | ALL SIZE | 2 hr 480 ℃ | 750~960 | 5~30 | 48~60 | B95~102 |
Product Photo:
Key Technology of Beryllium Copper(Heat treatment)
Age Hardening
Age hardening significantly enhances the material’s strength. This reaction is generally carried out at temperatures between 260°C and 540°C depending on alloy and desired characteristics. This cycle causes the dissolved beryllium to precipitate as a beryllium rich (gamma) phase in the matrix and at the grain boundaries. It is the formation of this precipitate which causes the large increase in material strength. The level of mechanical properties attained is determined by the temperature and time at temperature. It should be recognized that beryllium copper has no room temperature aging characteristics.
FAQ:
Q1:What’s the advantages the Beryllium Copper of CUBERYLLIUM®?
A1: 1: The Biggest Coil weight could be reach 1200kg/Coil
2:We are the only one who melting by Vacuum semi-Continuous Furnace.
3:Surface further polishing for top clients.
Q2:
How
about
your
payment
terms?
A2:
Generally,
30%
as
deposit
by
T/T,
then
70%
should
be
paid
before
the
delivery.
Q3:
Why
you
melting
by
Vacuum
semi-Continuous
Furnace?
A3:Could
be
get
the
Cast
ingot
without
gas,smaller
segregation,
Grain
Refinement
Q4:
What's
the
payment
terms?
A4:
We
accept
T/T,
L/C,
Paypal
etc.
It
can
be
negotiated
when
the
amount
is
different.