Translucent Liquid Platinum Cure Silicone Rubber RTV2 Silicone For Soap Candle Mold

Price	USD 5.98~6.48 KG
MOQ	120kg
Delivery Time	3-5 working days after payment
Brand	MC silicone
Place of Origin	CHINA
Certification	MSDS,SGS
Model Number	MCPLA-L20A/B
Packaging Details	20kg;200KG/DRUM
Payment Terms	L/C, D/P, T/T, Western Union
Supply Ability	4000KG PER DAY

Product Details

Product Specification

Working time	30~40 minutes(Adjustable)	Mixed Viscosity	7000-9000 cps(Adjustable)
Curing time	4~6 hours (Adjustable)	Place of Origin	CHINA
Packaging Details	20kg;200KG/DRUM	Color	Translucent
Shelf life	12 months	Model Number	MCPLA-L20A/B
Mix ratio	1:1 by weight	Hardness	20 shore A
Supply Ability	4000KG PER DAY	Certification	MSDS,SGS
Brand Name	MC silicone	Payment Terms	L/C, D/P, T/T, Western Union
Price	USD 5.98~6.48 KG	Delivery Time	3-5 working days after payment
Goods description	Translucent Platinum Liquid Silicone Rubber	Minimum Order Quantity	120kg
Features	odor-free, food safe, easy to use	shrinkage	0.1%
Elongation	600%

Product Description

Platinum Cure Translucent Liquid Silicone Rubber RTV2 Silicone Raw Material For Soap, Candle Mold Making

MCPLA-L20A/B are platinum-cured (also known as addition-cure), room temperature-curing silicones that cure to flexible, high-strength rubbers. MCPLA-L20A/B molds offer excellent release properties and release agent is not necessary when casting most materials.

Features

High tear and tensile strength

Long shelf life with low shrinkage

Fast mixing (1 :1)

Easy processing due to the low viscosity

Self-release properties

Bubble Free

Food safe, Skin safe,Eco-friendly

Applications

Molding applications requiring low shrinkage e.g., jewelry, automotive, plaster, cement, cake decorations,food molds, Soap, Candle molds,etc.

Processing and Instructions of Addition Cure Silicones

1. Mixing the two components

According the mixing ration 10:1 or 1:1 weighting A and B, the two components may be thoroughly mixed either by hand or using a low-speed electric to minimize the degassing of bubbles and to avoid any temperature increase. Note: It is also possible to use a special mixing and dispensing machine for the silicone components, further information is available upon request.

2. Moulding

The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing. The silicone mixture expands to 3-4 times of its initial volume and bubbles rise to the surface. The bubbles progressively disappear and the mixture returns to its initial volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure.

Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter/height ratio (3 to 4 times of the initial volume)

3. Polymerisation

The curing may be slowed down at lower temperature or accelerated by applying heat.

Note:

Contamination from sulfur (e.g., sulfur-based clay), amines, tin compounds, cured polyester resin, some paints and some silicone rubbers may inhibit surface cure of platinum-cured rubbers.

Apply a release agent, Although not usually necessary, a release agent will make demolding easier when casting into most surfaces.

Storage and shelf life
MC Silicone MCPLA -L Series should be used within 12 months from the manufacturing date. Beyond this date, MC silicone no longer guarantees the products confirms with the sales Specification. In order to preserve best properties it is recommended to follow strictly the following guild lines:
Store the original packing tightly sealed and at a temperature below 30 degree Celsius.
Use the product as soon as the packaging has been opened.

Packaging

20kg per drum, 200kg per drum

Technical Properties

Item No.	MCPLA-L20A/B silicone rubber
Appearance	Transparent Viscous liquid
Color	Translucent
Viscosity ( cps,approx.)	7000-9000
Mix ratio (A:B)	1:1
Working time(at 25℃ ,minutes)	30-40
Curing time(at 25℃,hrs,approx.)	4~6
Hardness Shore A(after 24 h)	20
Tensile Strength(Mpa,after 24 h)	3.8
Elongation(%)	600
Tear Strength(N/mm)	16
Linear Shrinkage (%)	0.1

Certificate Guarantee

MINGCHENG GROUP LIMITED

Manufacturer of Silicone Fluids, Mould Making Silicones & Casting Materials

www.mcsilicone.com

Mob/Wechat/WhatsApp: 0086-19848097281

nicole@mcsilicone.com
Address:NO.2, ZHOULIAO ROAD, LANGZHOU INDUSTRIAL ZONE,CHANGPING, DONGGUAN, GUANGDONG, CHINA

Translucent Liquid Platinum Cure Silicone Rubber RTV2 Silicone For Soap Candle Mold

Product Details

Product Specification

Product Description

Platinum Cure Translucent Liquid Silicone Rubber RTV2 Silicone Raw Material For Soap, Candle Mold Making